ANALISIS ELEKTROPLATING
Kategori Coating | Singkatan Coating | warna | Ketebalan Coating | Perbandingan Kapabilitas Proteksi Lumahing Coating | Suhu Aplikasi sing Disaranake | Tension lumahing | ||
Uji Semprotan Garam Netral | Test Kelembapan Panas | Tes PCT | ||||||
Ni / Barrel Plating | Ni | Perak padhang | 10-20 | ☆☆☆☆☆ | ☆☆☆☆☆ | ☆☆☆☆☆ | ≤260 | 36 |
Ni/Rack Plating | Ni | Perak padhang | 10-20 | ☆☆☆☆ | ☆☆☆☆☆ | ☆☆☆☆☆ | ≤260 | 36 |
3+Cr Zn/Biru-Putih Zn/Laras Plating | Zn | Biru&putih | 5-10 | ☆☆☆☆ | ☆☆☆ | ☆☆☆ | ≤160 | 38 |
3+Cr Zn/Zn Biru-Putih/Rack Plating | Zn | Biru&putih | 5-10 | ☆☆☆ | ☆☆☆ | ☆☆☆ | ||
3+Cr Warna Zn/Laras Plating | Warna Zn | Werna padhang | 5-10 | ☆☆☆ | ☆☆☆ | ☆☆☆ | ||
3+Cr Warna Zn/Rack Plating | Warna Zn | Werna padhang | 5-10 | ☆☆☆ | ☆☆☆ | ☆☆☆ | ||
Ni + Kimia Ni Barrel Plating | Ni + Kimia Ni | Salaka peteng | 12-20 | ☆☆☆☆☆ | ☆☆☆☆☆ | ☆☆☆☆ | ≤200 | 36 |
Ni + Kimia Ni Rack Plating | Ni + Kimia Ni | Salaka peteng | 12-20 | ☆☆☆☆ | ☆☆☆☆☆ | ☆☆☆☆ | ||
Ni+Cr | Ni+Cr | Ireng peteng | 12-20 | ☆☆☆☆ | ☆☆☆☆☆ | ☆☆☆☆☆ | ≤260 | 36 |
Teflon | Teflon | werna abu-abu peteng |
| ☆☆☆ | ☆☆☆ | ☆☆☆ | ≤260 | 36 |
Ni + Ireng Ni | Ni + Ireng Ni | ireng | 12-20 | ☆☆☆☆☆ | ☆☆☆☆☆ | ☆☆☆☆☆ | ||
Ni+Sn | Ni+Sn | Perak padhang | 12-20 | ☆☆☆☆ | ☆☆☆☆☆ | ☆☆☆☆☆ | - | 36 |
Ni + Ag | Ni + Ag | salaka | 12-20 | ☆☆☆☆ | ☆☆☆☆☆ | ☆☆☆☆☆ | - | 36 |
Ni+Au | Ni+Au | emas | 10-20 | ☆☆☆☆ | ☆☆☆☆☆ | ☆☆☆☆☆ | - | 36 |
Epoksi | EPOXY | ireng | 10-20 | ☆☆☆☆☆ | ☆☆☆☆☆ | ☆☆☆☆ | ≤160 | 36 |
Ni/NiCu+Epoxy | NiCuNi/NiCu+EPOXY | ireng | 15-25 | ☆☆☆☆☆ | ☆☆☆☆☆ | ☆☆☆ | ≤160 | 36 |
Pasif / Fosfatisasi | Phosphoric / Pasif | werna abu-abu peteng | 1-3 | — | — | — | ≤240 | 37 |
Lapisan Nano | Lapisan nano | Werna abu-abu | 15-30 | ☆☆☆☆☆☆ | ☆☆☆☆☆☆ | ☆☆☆☆☆☆☆ | ≤300 | 33 |
KATEGORI
1. Lingkungan SST: 35 ± 2 ℃, 5% NaCl, PH = 6,5-7,2, Salt semprotan sinking 1,5ml / Hr.
2. Lingkungan PCT: 120±3 ℃, 2-2.4atm, banyu suling PH = 6.7-7.2, 100% RH
HUBUNGI KAMI kanggo panjaluk khusus